Hastelloy Fasteners
Natron Pipe Tube is a prominent manufacturer of Hastelloy Fasteners in India. Hastelloy encompasses a range of alloys mainly made up of nickel, molybdenum, and chromium. The distinctive formulation of these alloys provides exceptional resistance to both corrosion and high temperatures. Among them, Hastelloy C276 (2.4819) stands out as the most widely used grade for fasteners, known for its versatility and superior corrosion resistance, often outperforming in demanding environments.
Hastelloy Washers, Hastelloy Bolt, Hastelloy Alloy Nuts, Hastelloy Fasteners Supplier and Manufacturer in Mumbai, India
The demand for corrosion-resistant materials such as Hastelloy Fasteners significantly reduces the need for frequent replacements of basic components. Regular steel parts are prone to corrosion, leading to higher replacement costs. While Hastelloy Fasteners may have a higher initial expense, they prove to be more cost-effective for long-term applications due to their durability. Additionally, Hastelloy threaded rods exhibit excellent resistance in environments containing chlorine and fluorine ions, both of which are highly reactive halogens that can adversely affect standard metals.
Hastelloy Fasteners Specification
| Specifications | ASTM B574 / ASME SB574 |
| Standard | ASTM, DIN, BS |
| hastelloy Bolts Length in MM | 3 – 200 |
| hastelloy Nut & Bolt Sizes in Inch | M3 – M56 3/6 – 2 |
| hastelloy Screws Size | M1.6 – M12 |
| hastelloy Washers Size in Inch | M3 – M56 3/6 – 2 |
| hastelloy Grades | Hastelloy C276 Fasteners Hastelloy B2 Fasteners Hastelloy C22 Fasteners |
|---|
Hastelloy comprises a group of corrosion-resistant alloys, with nickel serving as a key component, which imparts exceptional resistance to acidic environments. Due to their outstanding durability against various acidic solutions—including hydrochloric acid, sulfuric acid, phosphoric acid, acetic acid, and formic acid Hastelloy fasteners are often recommended for use in industries such as textiles and paper manufacturing. These sectors frequently utilize these acids as leveling agents or for neutralizing solutions, making Hastelloy an ideal choice for their applications.
Hastelloy Fasteners Chemical Composition
| Element | Hastelloy C22 | Hastelloy C276 | Hastelloy B2 |
|---|---|---|---|
| Carbon | 0.01 Maximum | 0.01 Maximum | 0.02 Maximum |
| Manganese | 0.50 Maximum | 1.0 Maximum | 1.0 Maximum |
| Carbon monoxide | 2.5 Maximum | 2.5 Maximum | 1.0 Maximum |
| Sulfur | 0.02 Maximum | 0.03 Maximum | 0.03 Maximum |
| Silicon | 0.08 Maximum | 0.08 Maximum | 0.1 Maximum |
| Chromium | 20 To 22.5 | 14.5 To 16.5 | 1.0 Maximum |
| Molybdenum | 12.5 To 14.5 | 15 To 17 | 26 To 30 |
| Iron | 2 To 6 | 4 To 7 | 2.0 Maximum |
| Tungsten | 2.5 To 3.5 | 3 To 4.5 | – |
| Vanadium | 0.35 Maximum | 0.35 Maximum | – |
| Phosphorus | 0.02 Maximum | 0.04 Maximum | 0.04 Maximum |
Mechanical Properties Of Hastelloy Fasteners
| Element | Hastelloy C22 | Hastelloy C276 | Hastelloy B2 |
|---|---|---|---|
| Density | 8.69 g/cm3 | 8.89 g/cm3 | 9.2 g/cm3 |
| Melting Point | 1399 °C | 1370 °C | 1370 °C |
| Tensile Strength | Psi – 1,00,000, MPa – 690 | Psi – 1,15,000, MPa – 790 | Psi – 1,10,000, MPa – 760 |
| Yield Strength | Psi – 45000, MPa – 310 | Psi – 52,000, MPa – 355 | Psi – 51000, MPa – 350 |
| Elongation | 45 | 40 | 40 |
Hastelloy Fasteners Equivalent Grade
| Standard | Hastelloy C276 | Hastelloy C22 | Hastelloy B2 |
|---|---|---|---|
| UNS | N10276 | N06022 | N10665 |
| WERKSTOFF NR. | 2.4819 | 2.4602 | 2.4617 |
| JIS | NW 0276 | NW 6022 | – |
| GOST | ХН65МВУ | – | – |
| OR | ЭП760 | – | – |
| EN | NiMo16Cr15W | NiCr21Mo14W | – |